Overview
The resin is created by intruducing ethylene-propylene rubber inside semi-crystalline PP homopolymer matrix. It has high heat deformation temperature (HDT), good scratching resistance, good impact resistance at low temperature, good rigid-tough balance and good fluidity. Products made from this resin are characterized by fast processing and excellent processability.
Application
PP impact copolymer is widely used in the production of industrial products, such as dashboard, auto interior decorations, auto bumpers, interior and exterior parts of washing machine, accumulator containers and tanks. It can also be used to make household articles, such as bottle caps, cookware, furniture, toys, toolkits, travel cases, bags and various packaging containers.
Packages, Storage & Transportation
The resin is packaged in internally film-coated polypropylene woven bags or FFS film bags. The net weight is 25Kg/bag. The resin should be stored in a drafty, dry warehouse and away from fire and direct sunlight. It should not be piled up in the open air. During transportation, the material should not be exposed to strong sunlight or rain and should not be transported together with sand, soil, scrap metal, coal or glass. Transportation together with toxic, corrosive and flammable substance is strictly prohibited.
Grades and Typical Values (Not Warranted Values) and Applications
| Grades | K8003 | K8303 | K9026 | |
| MFR | g/10 min | 2.5 | 2.0 | 26.0 |
| Tensile Strength at Yield | MPa | 23.5 | 23.5 | 18.0 |
| Notched Izod Impact Strength | (23°C, KJ/m2) | – | – | 53 |
| (-20°C, KJ/m2) | 5.8 | 5.8 | – | |
| Flexural Modulus | MPa | 1310 | 1310 | 850 |
| Applications | Heavy Duty Parts, Automotive Parts | High-impact, Devices, Automotive Parts | Automotive Parts | |
| Grades | K9820H | K9829H | K7726H | K7735H | K7760H | K7780 | K7100 | |
| MFR | g/10 min | 19 | 27 | 29 | 40 | 60 | 80 | 110 |
| Ruber Component Content | % | 24 | 25 | – | – | – | – | 15.3 |
| Tensile Strength at Yield | MPa | 22.3 | 21.8 | 26.5 | 25.7 | 27.5 | 28.1 | 24.2 |
| Notched Izod Impact Strength | (23°C, KJ/m2) | 53 | 49 | 12 | 11 | 9.9 | 8.4 | 7.2 |
| (-20°C, KJ/m2) | 12 | 9 | 6.2 | 6.1 | 5.0 | 3.8 | 3.7 | |
| Flexural Modulus | MPa | 1118 | 1029 | 1328 | 1355 | 1300 | 1399 | 1322 |
| Applications | High-Impact Devices, Automotive and Household Appliances Parts | High-Impact Devices, Automotive and Household Appliances Parts | Washing Machine Barrel and Parts | Washing Machine Barrel and Parts | Washing Machine Barrel and Parts | High-Impact Devices, Automotive and Household Appliances Parts | High-Impact Devices, Automotive and Household Appliances Parts | |
| Grades | EPS30R (Qil) | EPS30RA | SP179 | EPS30R (Tia) | M700R | M180R | M2600R | M3000RH | |
| MFR | g/10 min | 1.5 | 2.5 | 10 | 1.5 | 7 | 1.8 | 26 | 30 |
| Tensile Strength at Yield | MPa | 24 | 24 | 19 | 22 | 31 | 21.6 | 24.5 | 15 |
| Notched Izodimpact Strength | (23°C, KJm2) | – | – | – | 320(J/m) | 15 | 29.5 | 43 | 5 |
| (-20°C, KJm2) | 4 | 5 | 7 | 45 (J/m) | – | – | 27 | 2 | |
| Flexural Modulus | MPa | 950 | 750 | 700 | 900 | 1100 | 900 | 1200 | 800 |
| Applications | Heavy Duty Parts, Automotive Parts | Heavy Duty Parts, Automotive Parts | Automotive Parts | Heavy Duty Parts, Automotive Parts | Shells of Automobiles and Cases batteries | Transfer Cases, Heavy Duty | Washing Machines Barrels | Scour Copolymerization | |
| Grades | EP200K | EP548R | EP300H | 2110H | 2240S | 2800J | K7926 | |
| MFR | g/10 min | 3.5 | 29 | 2 | 2.5 | 30 | 2.8 – 4.8 | 26 |
| Tensile Strength at Yield | MPa | 22 | 27 | 25 | 23 | 22 | 18 | 25 |
| Notched Izod Impact Strength | (23°C, KJm2) | 60 | – | – | 52 | 7 | 54 | – |
| (-20°C, KJm2) | – | 8 | 10 | – | – | – | 11 | |
| Flexural Modulus | MPa | 950 | 1450 | 1000 | 1050 | 1050 | 830 | 1200 |
| Applications | Packaging of food, stationery, shirts and etc (high transparency) | Food, cosmetics, clothing and cigarette packaging | Packaging of food, stationery, shirts and etc (high transparency) | Battery shell and other daily necessities | Barrels, boxes, container | Trunk, Toys | Household products, toys, household appliances | |
| Grades | EPT30R | PPB-M09 | HHP4 | PPB-MM35-S | PPB-MT25-S | PPB-MML28-S | PPB-M02D | HHP10 | PPB-M15-S | |
| MFR | g/10 min | 3.5 | 9.0 | 28.0 | 27 | 21 | 30 | 1.8 | 35 | 15.0 |
| Tensile Strength at Yield | MPa | 22 | 23 | 18 | 25 | 29 | 22 | 20 | 22 | 22 |
| Notched Izod Impact Strength | (23°C, KJm2) | 130 | 75 | 80 | 10 | – | – | 200 | 120 | 8 |
| Flexural Modulus | MPa | 900 | 950 | 900 | 1200 | – | 1150 | 900 | 1100 | 1050 |
| Applications | Toys, Shells of Storage Batteries | Household Appliances, Package | Thin Injection Molding Products | Washing Machine Barrels | Household Tranparent Injection Molding | Automotive Parts | Household Appliances, Packages | Washing Machine Barrels | Containers, Sundry Cases | |
| Grades | PPB-M02 (J340) | PPB-M02-V (K8003) | K9015 | YPJ-1215C | PPB-M20-V (YPJ-1220C) | YPJ-630 | YPJ-630H | M180RI | |
| MFR | g/10 min | 1.8 | 2.5 | 15 | 15 | 20 | 30 | 30 | 1.8 |
| Tensile Strength at Yield | MPa | 25 | 21 | 14 | 22 | 18 | 23 | 18 | 25 |
| Notched Izod Impact Strength | (23°C, KJm2) | 10 | 40 | – | – | 30 | 6 | 6 | 600 |
| (-20°C, KJm2) | 3 | 5 | – | 6 | 3.0 | 4 | 80 | ||
| Flexural Modulus | MPa | 1000 | 900 | 600 | 1030 | 800 | 1000 | 1000 | 900 |
| Applications | Toys, Shells of Storage Batteries | Toys, Shells of Storage Batteries | Automotive Parts | Automotive Parts | Automotive Parts | Scour Copolymerization | Scour Copolymerization | Transfer Boxes, Heavy Packages | |
| Grades | PPB-M09 | M30RH | M30RHC | M50RH | M60RHC | M50T | K7109 | K7116 | K7227 | |
| MFR | g/10 min | 9.2 | 30 | 30 | 50 | 60 | 53 | 8.5 | 20.1 | 31.2 |
| Tensile Strength at Yield | MPa | 25.4 | 24.3 | 24 | 26 | 39.5 | 26 | 23.6 | 23.1 | |
| Notched Izod Impact Strength | (23°C, KJm2) | 7.8 (23°C, J/m) | 8.4 (23°C, J/m) | 6 | 6 | 3 | 1.2 (23°C, J/m) | 11 | 14 | 11 |
| Flexural Modulus | MPa | 1120 | 1250 | 1500 | 1100 | 1500 | 2160 | 1220 | 1206 | 1210 |
| Grades | K8228 | K8003 | K8009 | K7727H | NBC03HRA | PPB-NS06 | PPB-KH39M | PPB-KH75M | |
| MFR | g/10 min | 28.6 | 3 | 8.5 | 29 | 32 | 0.9 | 60 | 70 |
| Tensile Strength at Yield | MPa | 24.2 | 21 | 21 | 25 | 20 | 9.2 | 28.9 | 31 |
| Notched Izod Impact Strength | (23°C, KJm2) | 9.7 | 56 | 46 | 7.9 | 12 | – | 7.6 | 6.5 |
| Flexural Modulus | MPa | 1232 | 870 | 870 | 1200 | 850 | 225 | 1350 | 1530 |
| Grades | NAX9 | NAX6 | NAC5C | NAC4 | NAR6 | NAR3 | NBC02 | NBX05 WS | NBC03 HRA | |
| MFR | g/10 min | 0.5 | 2.5 | 3.3 | 7 | 2.2 | 9.5 | 23 | 45 | 32 |
| Tensile Strength at Yield | MPa | 18 | 18 | 15 | 20 | 18 | 18 | 19 | 12 | 21 |
| Notched Izod Impact Strength | (23°C, KJm2) | NB | NB | NB | 18 | NB | 8 | 20 | NB | 12 |
| Flexural Modulus | MPa | 300 | 330 | 590 | 770 | 560 | 480 | 900 | 450 | 1050 |