Overview
LLDPE injection-molding grade is white, nontoxic, tasteless and odorless, supplied in pellets. characterized by good fluidity, high tensile strength and toughness.
Application
LLDPE injection-molding grade is principally used for making household articles, such as plastic barrels, reusable plastic containers and large injection-molded. It can also be used to make color master batches and other functioning master batches.
Package, Storage & Transportation
The resin is packaged in internally film-coated polypropylene woven bags. The net weight is 25Kg/bag. The resin should be stored in a drafty, dry warehouse and away from fire and direct sunlight. It should not be piled up in the open air. During transportation, the material should not be exposed to strong sunlight or rain and should not be transported together with sand, soil, scrap metal, coal or glass. Transportation together with toxic, corrosive and flammable substance is strictly prohibited.
Grades and Typical Values (Not Warranted Values)
| Grades | M2720A | M2320 | 8916 | 8920 | 8008 | 8320 | 2020 | |
| MFR | g/10 min | 20 | 20 | 16 | 20 | 7.5 | 20 | 19 |
| Density | g/cm3 | 0.926 | 0.924 | 0.954 | 0.954 | 0.956 | 0.924 | 0.920 |
| Tensile Strength at Yield | MPa≥ | 12 | 12 | 24 | 10 | 25 | 10 | 9 |
| Tensile Strength at Break | MPa≥ | – | 8 | – | 90 | 200 | 4 | 6 |
| Tensile Strain at Break | %≥ | – | 300 | – | – | – | 50 | – |
| Brittleness Temperature (F50) | °C≤ | -70 | -60 | -70 | – | – | -60 | – |
| Grades | EGM-18H | YLJ-2520 | 2650 | M2320 | M2330D | M2790D | |
| MFR | g/10 min | 20 | 20 | 50 | 20 | 30 | 85 |
| Density | g/cm3 | 0.954 | 0.925 | 0.926 | 0.924 | 0.924 | 0.926 |
| Tensile Strength at Yield | MPa≥ | 26 | 9.0 | 8.6 | 10 | 6 | – |
| Tensile Strength at Break | MPa≥ | 14 | – | – | – | – | – |
| Tensile Strain at Break | %≥ | 180 | 500 | – | 600 | – | – |
| Brittleness Temperature (F50) | °C≤ | -75 | – | – | – | – | – |